AROPOL M 105 TB CS
AROPOL M 105 TB is a thixotropic, pre-accelerated, ortophthalic based polyester resin, with a moderate geltime.
Blog
What We Offer
By Category
By Manufacturer
0
| Property (postcured 24h at 50 C) | Value | Unit | Method |
| Tensile strength | 55 | MPa | ISO 527 |
| Tensile modulus | 3600 | MPa | ISO 527 |
| Elongation at break | 2,0 | % | ISO 527 |
| Flexural strength | 90 | MPa | ISO 178 |
| Flexural modulus | 4100 | MPa | ISO 178 |
| Heat deflection temperature (HDT) | 66 | C | ISO 75/2 (A) |
| Hardness | 45 | Barcol | ASTM D2583 |
| Water absorption, 24 hours | 19 | mg/sample* | ISO 62-80 |
| Water absorption, 28 days | 92 | mg/sample* | ISO 62-80 |
| * sample 50x50x4 mm | |||
Application
AROPOL M 105 TB resin is suitable for spray-up, hand lay-up and filament winding methods for manufacturing numerous FRP products for the marine, building and construction and transportation markets.
When applying AROPOL M 105 TB resin, styrene emission is reduced by up to 50% compared to standard resins. Emission is only 2-5% of polyester resin used compared to 5-10% of standard polyester resin. Excellent glass fiber wet out properties and easiness of application is characteristic for AROPOL M 105 TB.